Toothpaste Abrasion and Abrasive Particle Content: Correlating High-Resolution Profilometric Analysis with Relative Dentin Abrasivity (RDA).

In this in vitro study, the influence of the concentration of abrasive particles on the abrasivity of toothpastes was investigated using laser scan profilometry on polymethyl methacrylate (PMMA) surfaces with the aim of providing an alternative method to developers for screening of new toothpaste formulations. PMMA plates were tested in a toothbrush simulator with distilled water and four model toothpastes with increasing content of hydrated silica (2.5, 5.0, 7.5, 10.0 wt%). The viscosity of the model toothpaste formulations was kept constant by means of varying the content of sodium carboxymethyl cellulose and water. The brushed surfaces were evaluated using laser scan profilometry at micrometer-scale resolutions, and the total volume of the introduced scratches was calculated along with the roughness parameters Ra, Rz and Rv. RDA measurements commissioned for the same toothpaste formulations were used to analyze the correlation between results obtained with the different methods. The same experimental procedure was applied to five commercially available toothpastes, and the results were evaluated against our model system. In addition, we characterize abrasive hydrated silica and discuss their effects on PMMA-sample surfaces. The results show that the abrasiveness of a model toothpaste increases with the weight percentage of hydrated silica. Increasing roughness parameter and volume loss values show good correlation with the likewise increasing corresponding RDA values for all model toothpastes, as well as commercial toothpastes without ingredients that can damage the used substrate PMMA. From our results, we deduce an abrasion classification that corresponds to the RDA classification established for marketed toothpastes.