Investigation of Poly(MM-EM-BM) as Nanosealing Materials in Oil-Based Drilling Fluids: Synthesis and Evaluation.
Article in ACS omega, 2023. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Not yet cited in PubMed.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
0 citing papers in PubMed.
No citing paper in PubMed yet.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
6 authors.
Funding
No grant is acknowledged in the PubMed record.
Abstract
Nanosealing technology has become the key to overcoming the wellbore instability problem in deep and ultradeep shale formations. In this Article, the terpolymer poly(MM-EM-BM) was synthesized from methyl methacrylate, ethyl methacrylate, and butyl methacrylate by a Michael addition reaction. The poly(MM-EM-BM) nanoparticles were investigated by Fourier transform infrared spectroscopy, laser scattering analysis, and thermogravimetric analysis. The results imply that the particle size range of poly(MM-EM-BM) is between 33.90 and 135.62 nm and the average diameter is about 85.95 nm at room temperature, which can maintain excellent stability at 382.75 °C. The effects of poly(MM-EM-BM) on the properties of oil-based drilling fluids (OBDFs) were ascertained through experiments on the rheological performance, electrical stability, and high-temperature and high-pressure (HTHP) filtration loss. The results suggested that when the amount of added poly(MM-EM-BM) increases, the apparent viscosity, plastic viscosity, dynamic shear force, and demulsification voltage of the drilling fluids will increase correspondingly; in contrast, the HTHP filtration loss gradually decreased. When poly(MM-EM-BM) is added at 0.75%, the kinetic-to-plastic ratio of the drilling fluids is 0.24 and the filtration loss is 0.6 mL, showing excellent overall performance. The drilling fluids have a good rock-carrying ability and water loss wall-building property. The sealing performance and mechanism of poly(MM-EM-BM) were researched by the method of a sealing performance test under high temperature. The results indicated that the more poly(MM-EM-BM) used, the higher the sealing efficiency of the mud cake and the core as the sealing medium. When poly(MM-EM-BM) was added at 0.75%, the sealing rates of the mud cake and the core as the sealing medium reached the maximum sealing rates of 40.30% and 91.48%, respectively. When poly(MM-EM-BM) enters the core nanopore joint for a certain distance under formation pressure, a tight sealing layer will be formed to effectively prevent the entry of filtrate. Poly(MM-EM-BM) as a potential oil-based nanosealing agent is expected to solve the problem caused by wellbore instability in shale horizontal wells.