ArticlePolymers2023
Effect of Flame Treatment on Bonding Performance of GF/EP Pultrusion Sheets Used for VARI Process.
Article in Polymers, 2023. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Not yet cited in PubMed.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
0 citing papers in PubMed.
No citing paper in PubMed yet.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
6 authors.
Funding
Abstract
This paper presents an easy and low-cost flame treatment method to improve the bonding performance of GF/EP (Glass Fiber-Reinforced Epoxy) pultrusion plates, which are using widely for large size wind blades. In order to explore the effect of flame treatment on the bonding performance of the precast GF/EP pultruded sheet vs. the infusion plate, the GF/EP pultruded sheets were treated with different flame treatment cycles and were embedded in the fiber fabrics during the vacuum-assisted resin infusion process (VARI). The bonding shear strengths were measured by tensile shear tests. It is found that after 1, 3, 5, and 7 flame treatments, the tensile shear strength between the GF/EP pultrusion plate and infusion plate increased by 8.0%, 13.3%, 22.44%, and -2.1%, respectively. This indicates that the maximum tensile shear strength can be obtained after five times of flame treatment. In addition, DCB and ENF tests were also adopted to characterize the fracture toughness of the bonding interface with the optimal flame treatment. It is found that the optimal treatment gives increments of 21.84% and 78.36% for G I C and G II C, respectively. Finally, the surficial topography of the flame-treated GF/EP pultruded sheets were characterized by optical microscopy, SEM, contact angle test, FTIR, and XPS. The results show that flame treatment plays an impact on the interfacial performance through the combination of physical meshing locking and chemical bonding mechanism. Proper flame treatment would remove the weak boundary layer and mold release agent on the surface of the GF/EP pultruded sheet, etch the bonding surface and improve the oxygen-containing polar groups, such as C-O and O-C=O, to improve the surface roughness and surface tension coefficient of pultruded sheet to enhance the bonding performance. Excessive flame treatment destroys the integrity of epoxy matrix on bonding surface which results into the exposure of the glass fiber, and the carbonization of release agent and resin on the surface loosen the surficial structure, which reduces the bonding properties.