Numerical Analysis of a Transtibial Prosthesis Socket Using 3D-Printed Bio-Based PLA.

Lower-limb prosthesis design and manufacturing still rely mostly on the workshop process of trial-and-error using expensive unrecyclable composite materials, resulting in time-consuming, material-wasting, and, ultimately, expensive prostheses. Therefore, we investigated the possibility of utilizing Fused Deposition Modeling 3D-printing technology with inexpensive bio-based and bio-degradable Polylactic Acid (PLA) material for prosthesis socket development and manufacturing. The safety and stability of the proposed 3D-printed PLA socket were analyzed using a recently developed generic transtibial numeric model, with boundary conditions of donning and newly developed realistic gait cycle phases of a heel strike and forefoot loading according to ISO 10328. The material properties of the 3D-printed PLA were determined using uniaxial tensile and compression tests on transverse and longitudinal samples. Numerical simulations with all boundary conditions were performed for the 3D-printed PLA and traditional polystyrene check and definitive composite socket. The results showed that the 3D-printed PLA socket withstands the occurring von-Mises stresses of 5.4 MPa and 10.8 MPa under heel strike and push-off gait conditions, respectively. Furthermore, the maximum deformations observed in the 3D-printed PLA socket of 0.74 mm and 2.66 mm were similar to the check socket deformations of 0.67 mm and 2.52 mm during heel strike and push-off, respectively, hence providing the same stability for the amputees. We have shown that an inexpensive, bio-based, and bio-degradable PLA material can be considered for manufacturing the lower-limb prosthesis, resulting in an environmentally friendly and inexpensive solution.