Compressive Strength of Mineral Trioxide Aggregate with and without Disodium Hydrogen Phosphate at Different Mixing Ratios.
Article in Iranian endodontic journal, 2018. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 1 paper, 1 of them a synthesis that pooled it.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
1 citing paper in PubMed, 1 synthesis or guideline pooled it.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
6 authors.
Funding
No grant is acknowledged in the PubMed record.
Abstract
Introduction: Mineral Trioxide Aggregate Methods and Materials: One hundred and twenty samples were prepared with a two-piece stainless steel mold with a height of 6 mm and a diameter of 4 mm in order to evaluate the compressive strength where WMTA was used in 60 samples and DHP in white MTA composition (DHPWMTA) was used in other 60 samples. The compressive strength of WMTA and DHPWMTA was measured in various ratios of liquid to powder including 50, 60 and 70% and at 24 h and 21 days ( Results: The maximum and minimum compressive strength of WMTA groups were 63.25±1.96 (50% ratio and 21 days) and 37.79±1.28 (70% ratio and 24 h), respectively. The maximum and minimum compressive strength of DHPWMTA groups were 63.96±1.40 (60% ratio and 21 days) and 37.37±1.62 (70% ratio and 24 h), respectively. The effect of each of factors (type of material, powder to liquid ratio and time) alone were significant on the compressive strength ( Conclusion: Adding 2.5 wt% of DHP to white MTA increased samples compressive strength. Compressive strength in liquid to powder ratios of 50 and 60% compare to 70% and at 21 days compared to 24 h was high.