A Systematic Investigation on the Influence of Intumescent Flame Retardants on the Properties of Ethylene Vinyl Acetate (EVA)/Liner Low Density Polyethylene (LLDPE) Blends.
Article in Molecules (Basel, Switzerland), 2023. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 1 paper.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
1 citing paper in PubMed.
- Article
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
2 authors.
Funding
No grant is acknowledged in the PubMed record.
Abstract
Because of their high filler loadings, commercial-grade clean flame-retardant materials have unstable mechanical properties. To address this issue, intumescent polymers can be used to develop clean flame retardants with very low levels of smoke and toxicity generation. An intumescent flame retardant (IFR) system composed of red phosphorus (RP), zinc borate (ZB), and a terpolymer of ethylene, butyl acrylate, and maleic anhydride (EBM) was used to prepare EVA (ethylene-vinyl acetate) and EVA/LLDPE (linear low-density polyethylene) composites; their mechanical and flammability properties were systematically investigated. The limiting oxygen index (LOI) of the EVA/LLDPE (as base material) composite containing RP and ZB mixed with nonhalogenated flame retardant, mainly magnesium hydroxide (MH) and coadditives, including processing aids and thermal stabilizers, was established. RP was found to have little effect on the tensile properties of EVA/LLDPE 118W/120 phr flame-retardant (MH + RP) composites. There was a minute difference in the effective trend of RP between tensile strength and elongation at break. Following the addition of ZB, the elongation at break of the composites gradually decreased with increasing RP content and then leveled off when the RP content was over 10 phr. Mechanical properties (elongation at break and tensile strength) can be best maintained at below 10 phr content of RP. The mechanical properties decreased with lower amounts of EBM content. In addition, flame retardancy increased when the EBM content decreased. The findings further revealed that MH and RP have poor compatibility, yielding poor mechanical properties. The LOI greatly increased with RP content, even though the total content of flame retardants (main + intumescent flame retardant) was the same in all formulations. Only over 5 phr RP content formulations passed V-0 of the UL-94 test. When under 5 phr, the RP content formulations did not pass V-0 of the UL-94 test.