Design and tribological performance of short S-Glass fibre reinforced biocomposites on the influence of fibre length and concentration.
Article in Scientific reports, 2023. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 1 paper.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
1 citing paper in PubMed.
- Mechanical and Ballistic Properties of Epoxy Composites Reinforced with Babassu Fibers (Polymers · 2024Article
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
5 authors.
Funding
No grant is acknowledged in the PubMed record.
Abstract
Fibre-reinforced biocomposites usage has gained prominence over the past decade. Although higher fracture toughness was observed when fibres were added to biocomposites, material degradation could occur due to filler and fibre content intolerance in the biocomposite matrix. Optimisation of resin-fibre-filler ratios helps in increasing the tribological performance of high load-bearing applications. However, the tribological performance is less understood due to limited in-vitro studies on the effect of fibre microstructures. A comprehensive investigation of the reciprocating and rotary wear behaviour of different compositions was carried out by varying fibre (0%, 5%, 10% and 15%) to particulate filler (40%, 45%, 50%, and 55%) weight fractions. The investigation aimed to identify the optimal composition of fibre-reinforced biocomposites based on the in-vitro ball-on-disc reciprocating and rotary wear tests in the presence of modified Fusayama solution. The cross-sectional areas of wear tracks were analysed using laser microscopy and scanning electron microscopy techniques to assess the surface morphology and subsurface damage of the wear tracks on biocomposites and the antagonist. The numerical results were statistically analysed using two-way ANOVA followed by a posthoc Tukey's test (p = 0.05). The results showed a combination of adhesive, abrasive and fatigue wear for all the tested Groups. The friction coefficient had a longer transient period for the 5 wt% and 10 wt% Groups. Based on the surface roughness, coefficient of friction, SEMs, specific wear rate, and ease of manufacturing, the threshold limit for fibre loading was found to be 10 wt%. The rotary test had a considerably lower specific wear rate compared to the reciprocating test. Fibre weight fraction was found to be the influencing factor of the abrasive wear behaviour compared to fibre length for the tested Groups.