Analysis and Modeling of Aged SAC-Bi Solder Joints Subjected to Varying Stress Cycling Conditions.
Article in Materials (Basel, Switzerland), 2023. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 1 paper.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
1 citing paper in PubMed.
- Phase Equilibria of the Ag-Al-Au Ternary System and Interfacial Reactions in the Au-Materials (Basel, Switzerland) · 2023Article
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
7 authors.
Funding
No grant is acknowledged in the PubMed record.
Abstract
Solder joints are subjected to varied stress cycle circumstances in the electronic packaging service life but are also influenced by aging. There has been limited investigation into the influence of aging and varying cycles on SnAgCu-Bi (SAC-Bi) solder joint fatigue. Cyclic fatigue tests were performed on solder joints of several alloys, including SnAgCu (SAC305), SnAgCu-Bi (SAC-Q), and SnCu-Bi (SAC-R). Individual solder joints were cycled under varying stress levels, alternating between mild and harsh stress levels. At least seven samples were prepared for each alloy by alternating between 25 mild stress (MS) cycles and three harsh stress (HS) cycles until the solder joint broke off. The impact of aging on Bi-doped solder joints fatigue under varied amplitude stress was examined and predicted for 10 and 1000 h under 125 °C. Because of the "Step-up" phenomenon of inelastic work, a new fatigue model was developed based on the common damage accumulation (CDA) model. The experimental results revealed that aging reduced the fatigue life of the tested solder alloys, particularly that of SAC305. According to the CDA model, all solder alloys failed earlier than expected after aging. The proposed model uses the amplification factor to assess inelastic work amplification after switching between the MS and HS cycles under varying stress amplitude conditions. The amplification factor for the SAC-Bi solder alloys increased linearly with fracture initiation and substantially followed crack propagation until the final failure. Compared with existing damage accumulation models, the proposed fatigue model provides a more accurate estimation of damage accumulation. For each case, the cut-off positions were examined. The SAC-Q amplification factor increased linearly to 83% of its overall life, which was much higher than that of SAC305 and SAC-R. This study identified three distinct failure modes: ductile, brittle, and near intermetallic compound (IMC) failure. It was also observed that SAC-Q with an organic solderability preservatives (OSP) surface finish was more susceptible to brittle failure owing to the excessive brittleness of the alloy material.