ArticlePolymers2022
Rubber-Composite-Nanoparticle-Modified Epoxy Powder Coatings with Low Curing Temperature and High Toughness.
Article in Polymers, 2022. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 5 papers.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
5 citing papers in PubMed.
- Article
- Article
- Study of the Self-Polymerization of Epoxy/Phthalonitrile Copolymers and Their High-Performance Fiber-Reinforced Laminates.Polymers · 2023Article
- Synergistic Effect of Nanoparticles: Enhanced Mechanical and Corrosion Protection Properties of Epoxy Coatings Incorporated with SiOPolymers · 2023Article
- New Epoxy and Hardener System Based on an Imidazolium Ionic Liquid as an Anticorrosive Coating for Steel in the Marine Environment.ACS omega · 2023Article
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
6 authors.
Funding
Abstract
In this study, a rubber-composite-nanoparticle-modified epoxy powder composite coating with low curing temperature and high toughness was successfully fabricated. The effects of N,N-dimethylhexadecylamine (DMA) carboxy-terminated nitrile rubber (CNBR) composite nanoparticles on the microstructure, curing behavior, and mechanical properties of epoxy-powder coating were systematically investigated. SEM and TEM analysis revealed a uniform dispersion of DMA-CNBR in the epoxy-powder coating, with average diameter of 100 nm. The curing temperature of the epoxy-composite coatings had reduced almost 19.1% with the addition of 1phr DMA-4CNBR into the coating. Impact strength tests confirmed that DMA-CNBR-modified epoxy-composite coatings showed significant improvements compared with the neat EP coating, which was potentially attributed to the nanoscale dispersion of DMA-CNBR particles in epoxy coatings and their role in triggering microcracks. Other mechanical properties, including adhesion and cupping values, were improved in the same manner. In addition, thermal and surface properties were also studied. The prepared epoxy composite powder coating with the combination of low curing temperature and high toughness broadened the application range of the epoxy coatings.