ArticleMaterials (Basel, Switzerland)2022
Combined Influence of Lithium Nitrate and Metakaolin on the Reaction of Aggregate with Alkalis.
Article in Materials (Basel, Switzerland), 2022. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 1 paper.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
1 citing paper in PubMed.
- Impact of Aggregate Grain Size on ASR-Induced Expansion.Materials (Basel, Switzerland) · 2023Article
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
1 author.
Funding
Abstract
The best known and effective methods for the reduction of the negative effects of an alkali-silica reaction in concrete include the application of mineral additives with an increased aluminium content and reduced share of calcium, as well as chemical admixtures in the form of lithium compounds. Because both aluminium and lithium ions increase the stability of reactive silica in the system with alkalis, it is possible to presume that the application of both corrosion inhibitors together will provide a synergistic effect in the ASR limitation. The paper presents the results of studies on the influence of combined application of metakaolin and lithium nitrate on the course of corrosion caused by the reaction of opal aggregate with alkalis. The potential synergistic effect was studied for the recommended amount of lithium nitrate, i.e., the Li/(Na + K) = 0.74 molar ratio and 5%, 10%, 15%, and 20% of cement mass replacements with metakaolin. The effectiveness of the applied solution was studied by measurements of mortars expansion in an accelerated test, by microstructure observations, and by determination of the ASR gels composition by means of SEM-EDS. The influence of metakaolin and the chemical admixture on the compressive and flexural strengths of mortars after 28 and 90 days of hardening were also analysed. The results of the studies revealed a synergistic effect for mixtures containing metakaolin at 15% and 20% cement replacement and lithium nitrate admixture in alkali-silica reaction expansion tests. It was found that corrosion processes in mortars with 5 and 10% levels of metakaolin became more severe after adding a lithium admixture to mortars with metakaolin only. The obtained results were confirmed by observations of the mortars' microstructures. There was no synergistic impact of lithium nitrate and metakaolin on compressive strength characteristics. The compressive strength of mortars containing a combination of metakaolin and lithium nitrate decreased both after 28 and after 90 days, compared to mortars with metakaolin alone.