Vinylated Modification of Biophytic Acid and Flame-Retardant/Crease-Proofing Finishing of Cotton Fabrics via In Situ Copolymerization.
Article in Materials (Basel, Switzerland), 2022. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 2 papers.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
2 citing papers in PubMed, 6 citations in OpenAlex.
- A Green P-N-Al Synergistic System for Eco-Friendly Flame-Retardant Polystyrene.Materials (Basel, Switzerland) · 2026Article
- Review
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
6 authors at 1 institution in 1 country.
Funding
No grant is acknowledged in the PubMed record.
Abstract
The vinyl phytic acid (GPA) was prepared using biophytic acid (PA) and glycidyl methacrylate (GMA), in which double bonds were introduced into the phytic acid molecule to increase the active groups in the phytic acid molecule. Furthermore, itaconic acid (IA) containing two unsaturated double bonds and GPA was polymerized in situ and crosslinked on the surface of cotton fabrics, and flame retardant and crease-proofed fabrics were obtained. The effects of GPA, IA, and the initiator on the flame-retardant and crease-proofing properties of the fabrics were analyzed by a single-factor and double-dip double-nip experiment. A flame-retardant and wrinkle-resistant fabric was obtained when the limiting oxygen index (LOI) and wrinkle recovery angle (WRA) were 28% and 270°, respectively. During combustion, the thermal properties of the fabrics changed; typically, the extrapolated initial temperature (Te) decreased, and moisture release increased. After burning, the fabrics had good shape retention, and the carbon residue content increased to 48%, which effectively inhibited or slowed down the combustion and heat release of the textiles. However, the whiteness, mechanical properties, and washability of the products need to be further improved.