The Influence of Annealing on the Microstructural and Textural Evolution of Cold-Rolled Er Metal.
Article in Materials (Basel, Switzerland), 2022. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Not yet cited in PubMed.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
0 citing papers in PubMed.
No citing paper in PubMed yet.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
10 authors.
Funding
Abstract
The microstructural and textural evolution of 60% cold-rolling-deformation Er metal (purity ≥ 99.7%) during annealing were investigated by electron-backscattered diffraction (EBSD) and X-ray diffraction (XRD). The research results showed that the texture of the (0001) plane orientation was strengthened, but there was no apparent enhancement of the (011¯0) and (1¯21¯0) plane orientations with increasing the annealing temperature. The recrystallization frequency and grain sizes gradually stabilized after the annealing duration of more than 1 h at 740 °C; the annealing duration and the recrystallization frequency were fitted to the equation: y=1 − exp (−0.3269x0.2506). HAGBs were predominant, and the distribution of grain sizes was the most uniform after annealing at 740 °C × 1 h, which was the optimal annealing process of the Er metal with 60% cold-rolling deformation. However, the recrystallization was transferred to the substructure due to grain boundary migration and twining under an excessive annealing temperature and duration.