Study on Microstructure and Properties of Black Micro-Arc Oxidation Coating on AZ31 Magnesium Alloy by Orthogonal Experiment.
Article in Materials (Basel, Switzerland), 2022. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Not yet cited in PubMed.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
0 citing papers in PubMed.
No citing paper in PubMed yet.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
5 authors.
Funding
No grant is acknowledged in the PubMed record.
Abstract
The effects of CuSO4 concentration, voltage and treating time on the hemisphere emissivity and corrosion resistance of AZ31B magnesium-alloy black micro-arc oxidation coatings were studied by orthogonal experiment. The microstructure, phase composition, corrosion resistance and hemisphere emissivity of the coating were investigated by scanning electron microscopy, energy-dispersive X-ray spectroscopy, X-ray diffraction, X-ray photoelectron spectroscopy, electrochemical test and infrared emissivity spectrometer, respectively. The results showed that the influences of each factor on corrosion current density and the hemisphere emissivity are as follows: voltage > treating time > CuSO4 concentration. The black MAO coatings are mainly composed of WO3, MgAl2O4, CuAl2O4, MgO, CuO and MgF2. The CuO and CuAl2O4 phases are the main reasons for blackness of the coatings. The coating exhibits the best corrosion resistance under the conditions of CuSO4 concentration 1.5 g/L, oxidation voltage 500 V and treating time 10 min. Additionally, the variation trends of hemispherical emissivity and roughness of the black MAO coating are the same when the composition of the coatings is similar. When the concentration of CuSO4 is 1.5 g/L, the oxidation voltage is 450 V and the treatment time is 10 min, the coating with the highest hemispherical emissivity of 0.84 can be obtained.