Ameliorating the stability of erbium-doped fiber laser using saturable absorber fabricated by the pulsed laser deposition technique.

In this paper, we present the performance and stability of an erbium-doped fiber laser (EDFL) based on ZnO saturable-absorber (SA) prepared using two schemes: solution method (SM) and pulsed laser deposition technique (PLDT). It was observed that EDFL with ZnO-SA prepared using SM emits at 1561.25 nm under a pump power of 230 mW. As the pump power is increased from 22.2 mW to 75.3 mW, the pulse duration decreases from 24.91 to 10.69 µs, and the pulse repetition rates increase from 11.59 to 40.91 kHz. Besides at pump power of 75.3 mW, the peak power, pulse energy, and average output power are measured as 0.327 mW, 2.86 nJ, and 0.18 mW, respectively. However, when PLDT-based SA was incorporated into the ring cavity, the emission wavelength is noticed at 1568.21 nm at a pump power of 230 mW. With the increase in pump power from 22.2 mW to 418 mW, the pulse repetition rates increase from 10.79 to 79.37 kHz and the pulse width decreases from 23.58 to 5.6 µs. Furthermore, the peak power, pulse energy, and average output power are observed to be 10.9 mW, 74 nJ, and 5.35 mW, respectively. The stability of EDFL based on SAs prepared using SM and PLDT has also been investigated. To the best of the author's knowledge, it is the first comparison of performance and long-term stability of EDFL based on two experimental techniques SM and PLDT-based SAs. These findings suggest that PLDT-based SAs provides optimum stability over a long period and enhanced the performance of fiber lasers compared to the SAs prepared using the conventional SM technique. This study paves the way for the development of ultra-stable SAs for their potential applications in pulsed laser sources and photonic devices.