Cu Nanowires and Nanoporous Ag Matrix Fabricated through Directional Solidification and Selective Dissolution of Ag-Cu Eutectic Alloys.
Article in Materials (Basel, Switzerland), 2022. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 1 paper.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
1 citing paper in PubMed.
- Ag and Sn Implications in 3-Polker Coins Forgeries Evidenced by Nondestructive Methods.Materials (Basel, Switzerland) · 2023Article
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
8 authors.
Funding
Abstract
Cu nanowires and a nanoporous Ag matrix were fabricated through directional solidification and selective dissolution of Ag-Cu eutectic alloys. Ag-39.9at.%Cu eutectic alloys were directionally solidified at growth rates of 14, 25, and 34 μm/s at a temperature gradient of 10 K/cm. The Cu phase in the Ag matrix gradually changed from lamellar to fibrous with an increase in the growth rate. The Ag matrix phase was selectively dissolved, and Cu nanowires of 300-600 nm in diameter and tens of microns in length were prepared in 0.1 M borate buffer with a pH of 9.18 at a constant potential of 0.7 V (vs. SCE). The nanoporous Ag matrix was fabricated through selective dissolution of Cu fiber phase in 0.1 M acetate buffer with a pH of 6.0 at a constant potential of 0.5 V (vs. SCE). The diameter of Ag pores decreased with increasing growth rate. The diameter and depth of Ag pores increased when corrosion time was extended. The depth of the pores was 30 μm after 12 h.