Crosslinker structure modulates bulk mechanical properties and dictates hMSC behavior on hyaluronic acid hydrogels.

Synthetic hydrogels are attractive platforms due in part to their highly tunable mechanics, which impact cell behavior and secretory profile. These mechanics are often controlled by altering the number of crosslinks or the total polymer concentration in the gel, leading to structure-property relationships that inherently couple network connectivity to the overall modulus. In contrast, the native extracellular matrix (ECM) contains structured biopolymers that enable stiff gels even at low polymer content, facilitating 3D cell culture and permeability of soluble factors. To mimic the hierarchical order of natural ECM, this work describes a synthetic hydrogel system in which mechanics are tuned using the structure of sequence-defined peptoid crosslinkers, while fixing network connectivity. Peptoid crosslinkers with different secondary structures are investigated: 1) a helical, molecularly stiff peptoid, 2) a non-helical, less stiff peptoid, and 3) an unstructured, relatively flexible peptoid. Bulk hydrogel storage modulus increases when crosslinkers of higher chain stiffness are used. In-vitro studies assess the viability, proliferation, cell morphology, and immunomodulatory activity of human mesenchymal stem cells (hMSCs) on each hydrogel substrate. Matrix mechanics regulate the morphology of hMSCs on the developed substrates, and all of the hydrogels studied upregulate IDO production over culture on TCP. Softer substrates further this upregulation to a plateau. Overall, this system offers a biomimetic strategy for decoupling hydrogel storage modulus from network connectivity, enabling systematic study of biomaterial properties on hMSC behavior and enhancement of cellular functionality for therapeutic applications. STATEMENT OF SIGNIFICANCE: Various strategies to tune hydrogel mechanics have been developed to control human mesenchymal stem cell (hMSC) behavior and regulate their immunomodulatory potential. However, these strategies typically couple mechanics to network connectivity, which in turn changes other hydrogel properties such as permeability that may have unintended effects on hMSC behavior. This work presents a strategy to tune hydrogel mechanics using crosslinkers with different secondary structure and molecular rigidity. This strategy successfully decouples hydrogel moduli from crosslinker stoichiometry and mimics the hierarchical nature of the native extracellular matrix. The moduli of the developed hydrogels led to significant impacts on hMSC morphology and proliferation, and increased immunomodulatory potential, indicating that molecular rigidity is a promising avenue to control engineered ECM mechanics for therapeutic applications.