Boron- and Boric Acid-Treated Titanium Implant Surfaces in Sheep Tibia: A Histologic, Histomorphometric and Mechanical Study.
Article in Bioengineering (Basel, Switzerland), 2022. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 3 papers.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
3 citing papers in PubMed, 5 citations in OpenAlex.
- Tetracalcium Phosphate Graft for Implant Stabilization: Resonance Frequency and Histomorphometric Analysis in a Sheep Tibia Model.Journal of functional biomaterials · 2026Article
- Boric Acid in Milk Replacer as a Health Enhancer and Growth Promoter for Lambs in the Suckling Period.Biological trace element research · 2025Article
- Dental Restorations.Bioengineering (Basel, Switzerland) · 2023Article
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
7 authors at 2 institutions in 1 country.
Funding
Abstract
The aim of this study was to compare the topographical, chemical and osseointegration characteristics of sandblasting and acid-etching (SLA) surfaces and dental implants treated by boron compounds. Titanium (Ti) disks (n = 20) were modified using boron (B) and boric acid (H3BO3) and then compared with the conventional SLA surface via surface topographic characterizations. Dental implants (3.5 mm in diameter and 8 mm in length) with the experimental surfaces (n = 96) were inserted into the tibias of six sheep, which were left to heal for 3 and 7 weeks. Histologic, histomorphometric (bone−implant contact (BIC%)) and mechanical tests (removal torque value (RTV)) were performed. The boron-coated surface (BC group) was smoother (Rz: 4.51 μm ± 0.13) than the SLA (5.86 μm ± 0.80) and the SLA-B (5.75 μm ± 0.64) groups (p = 0.033). After 3 weeks, the highest mean RTV was found in the SLA group (37 N/cm ± 2.87), and the difference compared with the BC group (30 N/cm ± 2.60) was statistically significant (p = 0.004). After 7 weeks, the mean RTV was >80 N/cm in all groups; the highest was measured in the H3BO3-treated (BS) group (89 N/cm ± 1.53) (p < 0.0001). No statistically significant differences were found in the BIC%s during both healing periods between the groups. H3BO3 seems to be a promising medium for dental implant osseointegration.