Effect of Low-Temperature Plasma Treatment on Starch-Based Biochar and Its Reinforcement for Three-Dimensional Printed Polypropylene Biocomposites.

Uniform dispersion and high interfacial adhesion are two of the most difficult components of creating an ideally reinforced polymer composite. One of the solutions could be surface engineering of reinforcing filler materials utilizing innovative technologies. Low-temperature plasma treatments in the presence of sulfur hexafluoride (SF6) gas are proposed as a sustainable alternative to modify the surface properties of biochar carbon synthesized from sustainable starch-based packaging waste via a high-temperature/pressure pyrolysis reaction in the current study. X-ray photoelectron spectroscopy tests revealed that plasma treatments were effective in the fluorination of biochar carbon like wet chemical methods. By delivering fluorine-related functionalities only on the surface of the carbon, plasma treatments were efficient in changing the surface properties of biochar carbon while keeping the carbon's beneficial bulk properties intact, which is unique to this method. The modified biochar was effectively utilized to reinforce polypropylene. Mechanical properties like tensile strength improved by 91% when compared to neat polymers and 31% when compared to untreated biochar-reinforced polymers at 0.75 wt % loadings. Elongation at break increased from 12.7 to 38.78, showing an impressive 216% increase due to effective reinforcement by plasma functionalization. The decomposition onset temperature and maximum rate of decomposition temperature increased by 60 and 49 °C, respectively, when compared to neat polymers. Plasma-modified biochar-reinforced three-dimensional printed samples have shown promise to be utilized for the development of composite parts using additive manufacturing methods.