Adhesive Strength in Dentin Conditioned with 18% Ethylenediaminetetraacetic Acid versus 35% Phosphoric Acid: In Vitro Study with 1-Year Artificial Aging.
Article in Polymers, 2022. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 5 papers.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
5 citing papers in PubMed, 7 citations in OpenAlex.
- Microbial interactions of EDTA: recent advances and biological applications in the context of natural product modulation.Frontiers in antibiotics · 2026Review
- Microtensile Bond Strength and Failure Mode of Different Universal Adhesives on Human Dentin.International dental journal · 2024Article
- Effect of Polywave and Monowave Light Curing Units on the Microtensile Bond Strength and Failure Types of Different Bulk-Fill Resin Composites: An in vitro Study.Clinical, cosmetic and investigational dentistry · 2024Article
- Microleakage in indirect onlay restorations cemented with three different types of adhesives: AnJournal of clinical and experimental dentistry · 2023Article
- Comparison of the Adhesive Remnant Index and Shear Bond Strength of Different Metal Bracket Bases on Artificially Aged Human Teeth: AnJournal of International Society of Preventive & Community DentistryArticle
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
8 authors at 5 institutions in 1 country.
Funding
No grant is acknowledged in the PubMed record.
Abstract
The success and longevity of a resin composite restoration is determined by its good bonding to the tooth structure, with the adhesion being a challenge to dentin due to its complexity and structural heterogeneity. The present study aimed to compare the adhesive strength of dentin conditioned with 18% ethylenediaminetetraacetic acid (EDTA) versus 35% phosphoric acid (H3PO4) in human premolars. Materials and Methods: This in vitro experimental study was performed on 40 human premolars. The occlusal thirds were sectioned and randomly placed into four groups according to the type of dentin conditioning: Group 1 (control), Group 2 (18% EDTA), Group 3 (35% H3PO4) and Group 4 (18% EDTA plus 35% H3PO4). Then, 10,000 thermocycles between 5 +/− 2 °C and 55 +/− 2 °C were applied. Adhesive strength was tested by shearing with a digital universal testing machine at a crosshead speed of 0.75 mm/min. The values obtained were analyzed in megapascals (MPa). The mean and standard deviation were used as measures of central tendency and dispersion. In addition, a one-factor intergroup ANOVA test was applied with Tukey’s post hoc test considering a significance level of p < 0.05. Results: The 18% EDTA and 18% EDTA plus 35% H3PO4 showed significantly higher adhesive strength compared to the control group that did not receive dentin conditioning (p = 0.047 and p < 0.001, respectively). However, the group conditioned with 18% EDTA did not present significant differences compared to the group conditioned with 35% H3PO4 (p = 0.997). In addition, the group conditioned with 18% EDTA plus 35% H3PO4 showed significantly higher adhesive strength compared to the groups conditioned with 18% EDTA (p = 0.002) and 35% H3PO4 (p = 0.001). Conclusion: The adhesion of bulk fill resin composite to dentin was favorable when preconditioning was performed using 18% EDTA followed by 35% H3PO4. In contrast, when both etchants were used separately, the bulk fill resin composite showed similar bond strength values in both cases, but significantly lower compared to their sequential application.