ArticleMaterials (Basel, Switzerland)2022
Optimization of Thermo-Mechanical Fatigue Life for Eutectic Al-Si Alloy by the Ultrasonic Melt Treatment.
Article in Materials (Basel, Switzerland), 2022. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 2 papers.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
2 citing papers in PubMed, 10 citations in OpenAlex.
- Improved Thermo-Mechanical Fatigue Resistance of Al-Si-Cu 319 Alloys by Microalloying with Mo.Materials (Basel, Switzerland) · 2023Article
- Thermo-Mechanical Fatigue Behavior and Resultant Microstructure Evolution in Al-Si 319 and 356 Cast Alloys.Materials (Basel, Switzerland) · 2023Article
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
7 authors at 1 institution in 1 country.
Funding
Abstract
The eutectic cast Al-Si alloys with excellent high-temperature and casting performance are widely used in engine pistons. During frequent starts and stops, the thermo-mechanical fatigue (TMF) is the most important failure cause. Ultrasonic melt treatment (UT) was chosen to compare and investigate the influence of micro-structures on fatigue life and damage mechanisms of as-cast (AC) eutectic Al-Si alloys under TMF loading. After UT, the grain size, primary Si, and intermetallic particles are reduced significantly in the alloy; fatigue life increases obviously. As a result of pilling-up of dislocations, the competitive effects of the critical strain/stress for fatigue crack nucleation can be found. There are two different crack initiation mechanisms under TMF: one is primary Si fracture for AC alloys with limited critical strain/stress for fatigue crack nucleation at fractured Si particles, and the other is primary Si debonding for UT alloys with increasing critical fracture strain/stress. After the crack initiation, the fractured or debonded primary phases provide the advantages for the further development of main cracks for both alloys. The UT alloy (805 ± 253 cycles) has about twice the TMF life of the AC alloy (403 ± 98 cycles). The refinement of micro-structures is instrumental in improving the fatigue resistance and life of TMF for the UT alloy.