Mechanical Properties of Polyvinyl Alcohol Fiber-Reinforced Cementitious Composites after High-Temperature Exposure.
Article in Gels (Basel, Switzerland), 2022. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 3 papers.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
3 citing papers in PubMed.
- Polyvinyl Alcohol-Modified NHL-Based Mortars for the Restoration of Historical Buildings.Materials (Basel, Switzerland) · 2026Article
- Preparation and properties of polyvinyl alcohol/calcium phosphate composite bone cement.The Journal of international medical research · 2025Article
- Article
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
5 authors.
Funding
Abstract
The mechanical properties of cementitious composites before and after exposure to high temperature are affected by calcium-silicate-hydrate (C-S-H) gels. To evaluate the effects of high temperature, plyvinyl alcohol (PVA) fiber content, and the cooling method on properties of cementitious composites, physical, mechanical, and microscopic tests were performed in this study. The target temperatures were 25, 100, 200, 300, 400, 600, and 800 °C. The PVA fiber contents were 0.0, 0.3, 0.6, 0.9, 1.2, and 1.5 vol%. The high-temperature resistance of PVA fiber-reinforced cementitious composite (PVA-FRCC) specimens was investigated through changes in their appearance, mass loss, compressive strength, splitting tensile strength, flexural strength, and microstructure. The results showed that PVA fibers reduced the probability of explosion spalling in the PVA-FRCC specimens exposed to high temperatures. The mass loss rate of samples exposed to temperatures below 200 °C was small and lower than 5%, whereas a significant mass loss was observed at 200 °C to 800 °C. A small rise in the cubic compressive and splitting tensile strengths of samples was found at 400 °C and 300 °C, respectively. Below 400 °C, the fibers were beneficial to the mechanical strength of the PVA-FRCC specimens. Nevertheless, when the temperature was heated above 400 °C, melted fibers created many pores and channels, which caused a decrease in the strength of the specimens. The method of cooling with water could aggravate the damage to the cementitious composites exposed to temperatures above 200 °C. High temperature could lead to the decomposition of the C-S-H gels of the PVA-FRCC samples, which makes C-S-H gels lose their bonding ability. From the perspective of the microstructure, the structure of PVA-FRCC samples exposed to 600 °C and 800 °C became loose and the number of microcracks increased, which confirmed the reduction in macro-mechanical properties.