Methylethynyl-Terminated Polyimide Nanofibrous Membranes: High-Temperature-Resistant Adhesives with Low-Temperature Processability.
Article in Polymers, 2022. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Not yet cited in PubMed.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
0 citing papers in PubMed, 3 citations in OpenAlex.
No citing paper in PubMed yet.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
7 authors at 1 institution in 1 country.
Funding
Abstract
As an alternative to traditional riveting and welding materials, high-temperature-resistant adhesives, with their unique advantages, have been widely used in aviation, aerospace, and other fields. Among them, polyimide (PI) adhesives have been one of the most studied species both from basic and practical application aspects. However, in the main applications of solvent-type PI adhesives, pinholes or bubbles often exist in the cured PI adhesive layers due to the solvent volatilization and dehydration reaction, which directly affect the adhesive performance. To address this issue, electrospun PI nanofibrous membranes (NFMs) were employed as solvent-free or solvent-less adhesives for stainless steel in the current work. To enhance the adhesion of PI adhesives to the metal substrates, phenolphthalein groups and flexible ether bonds were introduced into the main chain of PIs via the monomers of 4,4'-oxydiphthalic anhydride (ODPA) and 3,3-bis[4-(4-aminophenoxy)phenyl] phthalide (BAPPT). At the same time, the methylethynyl group was used as the end-capping component, and the crosslinking reaction of the alkynyl group at high temperature further increased the adhesive strength of the PI adhesives. Three kinds of methylethynyl-terminated PI (METI) NFMs with the set molecular weights of 5000, 10,000, and 20,000 g/mol were first prepared via the one-step high-temperature polycondensation procedure. Then, the PI NFMs were fabricated via the standard electrospinning procedure from the soluble METI solutions. The afforded METI NFMs showed excellent melt-flowing behaviors at high temperature. Incorporation of the methylethynyl end-capping achieved a crosslinking reaction at 280-310 °C for the NFMs, which was about 70 °C lower than those of the phenylacetylene end-capping counterparts. Using the METI NFMs as adhesive, stainless steel adherends were successfully bonded, and the single-lap shear strength (LSS) was higher than 20.0 MPa at both room temperature (25 °C) and high temperature (200 °C).