Attapulgite Structure Reset to Accelerate the Crystal Transformation of Isotactic Polybutene.
Article in Polymers, 2022. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 2 papers.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
2 citing papers in PubMed, 14 citations in OpenAlex.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
10 authors at 3 institutions in 1 country.
Funding
Abstract
Isotactic polybutene (iPB) has a wide application in the water pipe field. However, the most valuable form I, needs 7 days to complete the transformation. In this study, the attapulgite (ATP), which produces lattice matching of the iPB form I, was selected to prepare an iPB/ATP composite. The Fischer-Tropsch wax (FTW) was grafted with maleic anhydride to obtain MAFT, and the ATP structure was reset by reactions with MAFT to the prepared FATP, which improved the interface compatibility of the ATP and iPB. The Fourier transform infrared spectroscopy (FT-IR) and the water contact angle test confirmed the successful synthesis of FATP. X-ray diffraction (XRD) verified that the graft of MAFT did not affect the crystal structure of ATP. The iPB + 5% FATP had the maximum flexural strength, which was 12.45 Mpa, and the flexural strength of the iPB + 5% FATP annealing for 1 day was much higher than others. Scanning electron microscope (SEM) photographs verified that FATP and iPB had good interface compatibility. The crystal transformation behavior indicated that the iPB + 5% FATP had the fastest crystal transformation rate, which proved that the reset structure, ATP, greatly accelerated the crystal transformation of iPB. This was a detailed study on the effect of lattice matching, interfacial compatibility and internal lubrication of the reset structure, ATP, in the nucleation and growth stages of iPB form I. The result was verified by XRD, differential scanning calorimetry (DSC), Avrami kinetics and polarizing microscope (POM) analysis.