Synthesis of a Zinc Hydroxystannate/Sepiolite Hybrid Additive to Avoid Fire Propagation and Reduce Smoke Emission of EPDM Rubber Nanocomposites.

A zinc hydroxystannate/sepiolite (SEPZHS) hybrid additive was successfully prepared following a facile wet chemical route synthesis where zinc hydroxystannate (ZHS) nanoparticles were grown on the sepiolite's surface. SEPZHS particles have a fibrillar structure with ZHS nanoparticles homogeneously dispersed and with significantly smaller particle sizes than the synthesized ZHS nanoparticles alone. Sepiolite and SEPZHS were organically modified and introduced in a basic ethylene propylene diene monomer rubber (EPDM) formulation for cable to evaluate the nanocomposite behavior under direct fire sources. The results confirmed the synergistic effect of the hybrid SEPZHS additive in the formation of a most stable and efficient char barrier, thus improving the flame-retardant behavior of EPDM nanocomposite in terms of heat emission, with reductions of more than 40% in the peak of Heat Release Rate (cone calorimeter test), and smoke suppression, with more than 25% reduction in the Total Smoke Production and Smoke Density parameters (smoke chamber test). Moreover, the addition of sepiolite-based additives increased the mechanical properties (hardness) of the nanocomposites, as a result of the matrix reinforcement. This suggests that the SEPZHS hybrid additive may provide a promising option for a new, cost-effective, eco-friendly, yet efficient flame-retardant solution.