The Effect of an Er, Cr: YSGG Laser Combined with Implantoplasty Treatment on Implant Surface Roughness and Morphologic Analysis: A Pilot In Vitro Study.
Article in Journal of functional biomaterials, 2022. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 3 papers.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
3 citing papers in PubMed.
- Comparison of the efficacy of Er,Cr:YSGG laser on oral biofilm removal from implant surfaces with various application times for the treatment of peri-implantitis defects: ex vivo study.BMC oral health · 2024Trial
- Influence of peri-implantitis defect angles on morphology and the biocompatibility of the implant surfaces after Er, Cr: YSGG laser therapy: an ex vivo study.BMC oral health · 2026Article
- Impact of Er,Cr:YSGG Laser, Sandblast, and Acid Etching Surface Modification on Surface Topography of Biodental Titanium Implants.Journal of lasers in medical sciences · 2023Article
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
6 authors.
Funding
Abstract
Although laser irradiation and implantoplasty (IP) are both treatment options for peri-implantitis, no studies have yet combined these two treatment solutions. The aim of this study was to identify the effect of an Er, Cr: YSGG laser on the IP surface. In experiment 1, TiUnite anodized surface implants were treated with an Er, Cr: YSGG laser at 0.5 to 2 W on the panel energy setting and 20 Hz under water irrigation. In experiment 2, all implant surfaces were treated with the IP procedure first, then irradiated with the Er, Cr: YSGG laser. All samples were analyzed by stereomicroscopy, scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDS), and surface topography. Stereomicroscopy and SEM revealed no obvious surface change at any energy setting once the surface was polished with the IP procedure, whereas damage was caused to the TiUnite original implant surface when the Er, Cr: YSGG laser panel energy was set at 1 W or higher. EDS showed no significant difference in element composition once the surface was polished with the IP procedure, while a compositional change was detected when the Er, Cr: YSGG laser panel energy was set to 0.5 W or higher to irradiate the original TiUnite surface. Surface roughness may be related to laser irradiation energy, but no significant changes occurred following IP. These results indicated that the Er, Cr: YSGG laser may have little effect on the post-IP surface compared with the virgin TiUnite surface.