Computational wear of knee implant polyethylene insert surface under continuous dynamic loading and posterior tibial slope variation based on cadaver experiments with comparative verification.

backgroundThe effect of posterior tibial slope on the maximum contact pressure and wear volume of polyethylene (PE) insert were not given special attention. The effects of flexion angle, Anterior-Posterior (AP) Translation, and Tibial slope on the max contact pressure and wear of PE insert of TKR were investigated under loadings which were obtained in cadaver experiments by using Archard's wear law. This study uses not only loads obtained from cadaver experiments but also dynamic flexion starting from 0 to 90 degrees.

methodWear on knee implant PE insert was investigated using a 2.5 size 3 dimensional (3D) cruciate sacrificing total knee replacement model and Finite Element Method (FEM) under loadings and AP Translation data ranging from 0 to 90 flexion angles validated by cadaver experiments. Two types of analyses were done to measure the wear effect on knee implant PE insert. The first set of analyses included the flexion angles dynamically changing with the knee rotating from 0 to 90 angles according to the femur axis and the transient analyses for loadings changing with a certain angle and duration.

resultsIt is seen that the contact pressure on the PE insert decreases as the cycle increases for both Flexion and Flexion+AP Translation. It is clear that as the cycle increases, the wear obtained for both cases increases. The loadings acting on the PE insert cannot create sufficient pressure due to the AP Translation effect at low speeds and have an effect to reduce the wear, while the effect increases with the wear as the cycle increases, and the AP Translation now contributes to the wear at high speeds. It is seen that as the posterior tibial slope angle increases, the maximum contact pressure values slightly decrease for the same cycle.

conclusionsThis study indicated that AP Translation, which changes direction during flexion, had a significant effect on both contact pressure and wear. Unlike previous similar studies, it was seen that the amount of wear continues to increase as the cycle increases. This situation strengthens the argument that loading and AP Translation values that change with flexion shape the wear effects on PE Insert.