Controlled Release Mechanism of Vancomycin from Double-Layer Poly-L-Lactic Acid-Coated Implants for Prevention of Bacterial Infection.

Implantation failure due to bacterial infection incurs significant medical expenditure annually, and treatment tends to be complicated. This study proposes a method to prevent bacterial infection in implants using an antibiotic delivery system consisting of vancomycin loaded into poly-L-lactic acid (PLLA) matrices. A thin layer of this antibiotic-containing polymer was formed on stainless steel surfaces using a simple dip-coating method. SEM images of the polymeric layer revealed a honeycomb structure of the PLLA network with the entrapment of vancomycin molecules inside. In the in vitro release study, a rapid burst release was observed, followed by a sustained release of vancomycin for approximately 3 days. To extend the release time, a drug-free topcoat of PLLA was introduced to provide a diffusion resistance layer. As expected, the formulation with the drug-free topcoat exhibited a significant extension of the release time to approximately three weeks. Furthermore, the bonding strength between the double-layer polymer and the stainless steel substrate, which was an important property reflecting the quality of the coating, significantly increased compared to that of the single layer to the level that met the requirement for medical coating applications. The release profile of vancomycin from the double-layer PLLA film was best fitted with the Korsmeyer-Peppas model, indicating a combination of Fickian diffusion-controlled release and a polymer relaxation mechanism. More importantly, the double-layer vancomycin-PLLA coating exhibited antibacterial activity against