Coupling between γ-irradiation and synchrotron-radiation-based XAFS techniques for studying Mn-doped ZnO nanoparticles.
Article in Journal of synchrotron radiation, 2022. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 1 paper.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
1 citing paper in PubMed, 5 citations in OpenAlex.
- Comprehensive study of nanostructured BiRSC advances · 2024Article
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
4 authors at 3 institutions in 1 country.
Funding
Abstract
γ-Irradiation and synchrotron-radiation-based X-ray absorption fine-structure (XAFS) spectroscopy have been used to induce structure disorder through the interaction of γ-rays (200 kGy) with fabricated Mn-doped ZnO nanoparticles (NPs) and then to examine thoroughly the resultant structural change. The extracted electronic/fine XAFS structural parameters reflect a compositional and γ-irradiation co-dependence. The average crystal structure of samples prepared by the sol-gel method was investigated by X-ray diffraction (XRD). A detailed structural XRD data analysis was carried out by applying a Rietveld refinement using the MAUD program. XAFS spectra were collected at the Zn K-edge (9659 eV) in transmission mode and at the Mn K-edge (6539 eV) in fluorescence mode. Direct evidence of the solubility of Mn ions in the ZnO structure was demonstrated by fitting the extended-XAFS (EXAFS) signal. Near-edge XAFS (XANES) analysis provided the oxidation states of Zn and Mn ions through fingerprint XANES spectra of the sample along with those of standard compounds. Linear combination fitting showed that the most fit chemical forms of Zn and Mn in the samples are ZnO and MnO, respectively. The oxidation states of both Zn and Mn XAFS absorbers were confirmed from pre-edge fitting. The results of the magnetic measurements were explained in light of the average and electronic/local structural information obtained from XRD, XANES and EXAFS techniques. The magnetic properties of the samples translate into an induced change in the average crystal and electronic/local structures upon Mn concentration change and γ-irradiation. XRD confirmed the successful preparation of hexagonal Mn-doped ZnO NPs with a crystallite size in the range 33-41 nm. Both XRD and EXAFS analysis detected a minor amount of Mn