Micromechanism Study of Molecular Compatibility of PVDF/PEI Blend Membrane.

In this paper, the compatibility of polyetherimide (PEI) with different contents as a high-performance copolymer and polyvinylidene fluoride (PVDF) was studied, and 5%-20% PEI was prepared by the non-solvent-induced phase inversion method. The compatibility of PVDF and PEI was evaluated by analyzing the physical structure and properties of the blend membrane, the microstructure, the glass transition temperature Tg, the enthalpy, and the mechanism of the polymer blend enthalpy change. The results show that the blend membranes have -NH and C=O-N binding energies at X-ray photoelectron spectroscopy (XPS), which preliminarily proves that fluorine-amine bonds are formed between the polymers, and new spectra appeared by Fourier transform infrared (FTIR) and X-ray diffraction (XRD) peaks, which further proves that the two have the formation of fluorine-amine bonds, the Tg and enthalpy of the mixed membrane was increased, and a scanning electron microscope (SEM) observed that the membrane pores changed from finger-like pores to sponge-like macropores. When the content of PEI is 15%, the performance of the blended membrane is the best, the water contact angle increases to 58.5°, the porosity increases to 17.33%, the maximum force increases to 8.04 N, and the elongation at break decreases to 24.26%, the pure water flux is 1870.292 L/m