Assessment of the Influence of the Selected Range of Visible Light Radiation on the Durability of the Gel with Ascorbic Acid and Its Derivative.

(1) Background: Depending on the type of hydrophilic polymer used, different types of hydrogels may be chemically stable or may degrade and eventually disintegrate, or dissolve upon exposure to sunlight. Many over-the-counter medications are now stored with a limited control of temperature, humidity and lighting. Therefore, in this study, the photostability of a gel made of cross-linked polyacrylic acid (PA), methylcellulose (MC) and aristoflex (AV) was assessed, and the interaction between the polymers used and ascorbic acid and its ethylated derivative was investigated. (2) Methods: The samples were continuously irradiated at constant temperature for six hours. The stability of the substance incorporated into the gels was assessed using a UV-Vis spectrophotometer. FTIR-ATR infrared spectroscopy was used to measure changes during the exposure. (3) Results: Ascorbic acid completely decomposed between the first and second hours of illumination in all samples. The exception is the preparation based on polyacrylic acid with glycerol, in which the decomposition of ascorbic acid slowed down significantly. After six hours of irradiation, the ethylated ascorbic acid derivative decomposed in about 5% for the polyacrylic acid-based gels and aristoflex, and in the methylcellulose gel it decomposed to about 2%. In the case of ascorbic acid, the most stable formulation was a gel based on polyacrylic acid and polyacrylic acid with glycerol, and in the case of the ethyl derivative, a gel based on methylcellulose. (4) Conclusions: The experiment showed significant differences in the decomposition rate of both compounds, resulting from their photostability and the polymer used in the hydrogel.