Anti-Corrosion Performance of Migratory Corrosion Inhibitors on Reinforced Concrete Exposed to Varying Degrees of Chloride Erosion.
Article in Materials (Basel, Switzerland), 2022. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 2 papers.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
2 citing papers in PubMed.
- Cold-Sprayed Composite Metal-Fluoropolymer Coatings for Alloy Protection against Corrosion and Wear.Materials (Basel, Switzerland) · 2023Article
- Profile Change Law of Clad Rebars and the Formation Mechanism of Composite Interfaces during Hot Rolling.Materials (Basel, Switzerland) · 2022Article
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
6 authors.
Funding
Abstract
This study investigated the anti-corrosion performance of commercial amino alcohol migratory corrosion inhibitors (MCIs) on concrete that underwent varying degrees of chloride erosion. Electrochemical impedance spectroscopy (EIS), potentiodynamic polarization (PD), scanning electron microscopy, and energy dispersive spectroscopy (SEM-EDS) analyses were performed to study the anti-corrosion performance and mechanism of the MCIs on the steel bars. The results indicated that the corrosion resistance of the steel bars in concrete was significantly improved by coating with the MCIs, and the earlier the specimens were coated with the MCIs, the higher the anti-corrosion efficiency. The anti-corrosion efficiency was 55.35% when the MCIs coating was applied before chloride erosion; however, the anti-corrosion efficiency decreased to 3.40% when the MCIs coating was applied after the ninth drying-wetting cycle. The improvement in corrosion resistance of the steel bar in concrete coated with MCIs was due to the protective MCIs-molecule film that formed on the steel bar surfaces, and the oxidative dissolution of iron at the anode was effectively inhibited by the MCIs coating.