Powder Plasma Transferred Arc Welding of Ni-Si-B+60 wt%WC and Ni-Cr-Si-B+45 wt%WC for Surface Cladding of Structural Steel.
Article in Materials (Basel, Switzerland), 2022. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 6 papers.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
6 citing papers in PubMed.
- Surface Damage Regeneration in Railway Wheels.Materials (Basel, Switzerland) · 2026Article
- Article
- Composite Fe-Cr-V-C Coatings Prepared by Plasma Transferred-Arc Powder Surfacing.Materials (Basel, Switzerland) · 2023Article
- Experimental Comparison of Laser Cladding and Powder Plasma Transferred Arc Welding Methods for Depositing Wear-Resistant NiSiB + 60% WC Composite on a Structural-Steel Substrate.Materials (Basel, Switzerland) · 2023Article
- Impact of Titanium Addition on Microstructure, Corrosion Resistance, and Hardness of As-Cast Al+6%Li Alloy.Materials (Basel, Switzerland) · 2023Article
- High-Temperature Corrosion of Flame-Sprayed Power Boiler Components with Nickel Alloy Powders.Materials (Basel, Switzerland) · 2023Article
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
4 authors.
Funding
No grant is acknowledged in the PubMed record.
Abstract
Increasing demand for sustainable approaches to mining and raw material extraction, has prompted the need to explore advanced methods of surface modification for structural steels used in the extractive industry. The technology of powder plasma transferred arc welding (PPTAW), was used in this study as a surface modification technique to improve upon the abrasive wear resistance of structural steel grade EN S355. PPTAW process parameters, namely, plasma transferred arc (PTA) current and plasma gas flow rate (PGFR), were varied, and the effects of the variation were studied and used as criteria for selecting optimum conditions for further studies and parametric reproducibility. Two metal matrix composite (MMC) powders were used in the process, having compositions of Ni-Si-B+60 wt%WC (PG) and Ni-Cr-Si-B+45 wt%WC (PE). Microstructural observation under a scanning electron microscope (SEM) revealed a dendritic, multi-directional microstructure consisting of partially dissolved primary tungsten carbide particles and secondary tungsten carbide precipitates within the MMC solid solution. The hardness of the surface layers was higher than that of a reference AR400 steel by more than 263 HV. Final surface layers obtained from the MMC powders had abrasive wear resistance up to 5.7 times that of abrasion-resistant reference AR400 steel. Alloying the MMC matrix with chromium increased the hardness by 29.4%. Under the same process conditions, MMC powder with 60 wt% WC reinforcement had better abrasive wear resistance by up to 45.8% more than the MMC powder with 45 wt% WC.
Indexed as
Identifiers
What OpenQuestion holds
Registered trials
Read under generation 80e0d062 · epoch 390. Bibliography from PubMed, PubMed Central and OpenAlex; grants from NIH RePORTER; trial links from ClinicalTrials.gov; estimates, votes and beliefs from the OpenQuestion graph.