Facile Fabrication of Multifunctional Transparent Flame-Retarded Hydrogel for Fire-Resistant Glass with Excellent Transparency, Fire Resistance and Anti-Ageing Property.
Article in Polymers, 2022. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Not yet cited in PubMed.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
0 citing papers in PubMed, 12 citations in OpenAlex.
No citing paper in PubMed yet.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
4 authors at 1 institution in 1 country.
Funding
Abstract
Acrylamide-methacrylic acid copolymer named P (AM-co-MAA) was synthesized via aqueous solution polymerization, and then mixed with crosslinker, flame retardants and initiators to prepare multifunctional transparent flame-retarded hydrogels with transparency, fire resistance and anti-ageing property. The results show that the application of multifunctional transparent flame-retarded hydrogel imparts high level of transparency and excellent fire resistance to the fire-resistant glass, and the light transmittance and fire resistance of the flame-retarded hydrogel increases with the increasing mass ratio of AM to MAA in P(AM-co-MAA). When the mass ratio of AM to MAA is 4:1, the obtained P(AM-co-MAA) imparts the lowest backside temperature of 130 °C at 3600 s and highest light transmittance of 86.1% to the transparent flame-retarded hydrogel. TG and DSC analysis show that the addition of P(AM-co-MAA) increases the thermal stability of the transparent flame-retarded hydrogels due to the formation of numerous hydrogen bonds via the complexation between amide and carboxyl groups. Accelerated ageing test indicates that the transparent flame-retarded hydrogel containing P(AM-co-MAA) exerts durable fire resistance and transparency, and the ageing resistance of the transparent flame-retarded hydrogel depends on the mass ratio of AM to MAA in P(AM-co-MAA). Therefore, this study provides a promising strategy to prepare a novel multifunctional transparent flame-retarded hydrogel with excellent light transmittance, fire resistance and anti-ageing properties.