Surface Characteristics of Thermally Modified Bamboo Fibers and Its Utilization Potential for Bamboo Plastic Composites.

Bamboo fibers are considered as a more attractive option for the reinforcement of wood plastic composites as compared to wood fiber due to its fast growth rate and good toughness. Heat treatment is an environment-friendly method of improving the integrated performance of bamboo materials. This paper highlights the heat treatment of bamboo fiber for suitable properties as reinforcements in bamboo plastic composites. The effects of vacuum heat treatment on the surface characteristics of bamboo fibers and the properties of bamboo plastic composites were analyzed by studying the chemical composition, surface elements and polarity of bamboo fiber before and after treatment, and the physical and mechanical properties of bamboo plastic composite. The results showed that after vacuum heat treatment, the bamboo fibers became darker and experienced a transition from green to red. Moreover, FTIR, XPS and contact angle analysis indicated that the hemicellulose content, the oxygen/carbon ratio and the polar component of the bamboo fiber had a decreasing trend as the treatment temperature increased. In addition, the 24 h water absorption and the 24 h thickness expansion rate of the water absorption showed a trend of first decreasing and then increasing as the treatment temperature increased, while the bending performance of bamboo plastic composite showed a trend of increasing first and then decreasing as a result of increased treatment temperature. Therefore, a combined process of vacuum heat treatment and the addition of MAPE could improve the physical and mechanical properties of bamboo plastic composites to a certain extent.