ArticlePolymers2022
Effect of Different Pre-Treatment on the Microstructure and Intumescent Properties of Rice Husk Ash-Based Geopolymer Hybrid Coating.
Article in Polymers, 2022. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 2 papers.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
2 citing papers in PubMed, 30 citations in OpenAlex.
- Sustainable Aluminosilicate Coatings from Palm Oil Waste for Enhanced Thermal and Microstructure Properties.Materials (Basel, Switzerland) · 2025Article
- Thermal Properties and Drying Shrinkage Performance of Palm Kernel Shell Ash and Rice Husk Ash-Based Geopolymer Concrete.Materials (Basel, Switzerland) · 2024Article
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
7 authors at 3 institutions in 4 countries.
Funding
Abstract
Despite the growing popularity of rice husk ash (RHA) in various applications, limited research has been devoted to identify the influence of silica content in RHA on the intumescent properties. The present work aims to introduce a novel and economical geopolymer hybrid fire retardant coating by utilizing the use of RHA. The silica from Rice husk (RH) was extracted using distilled water and hydrochloric acid as leaching agents and subjected to pyrolysis treatment. X-ray fluorescence (XRF) analysis indicated that RH that underwent HCl pre-treatment at 600 °C for one hour produced a high purity amorphous silica content of 93.92%. XRD measurements revealed that HCl pretreatment increased the crystallization temperature of RHA to 1000 °C and retained the amorphous state of silica for 2 h. In a fire resistance test, temperature at the equilibrium and time taken to reach 200 °C for sample S3 (93.92% wt. silica) showed 5.83% and 3.48% improvement compared to sample S1 (87.49% wt. silica). The microstructure analysis showed that sample S1 possessed bigger pores on the coating surface while an increment in silica content in sample S3 produced a dense foam structure. Results from a fire resistance test were supported by the Energy dispersive X-ray (EDX) analysis of the sample. The oxygen-to-carbon ratio of S1 and S3 coating samples were 1.695 and 1.622 respectively, which indicated that lower oxygen-to-carbon ratio in sample S3 coating resulted in better anti-oxidant properties. Interestingly, the increment of SiO