Synthesis and Weak Hydrogelling Properties of a Salt Resistance Copolymer Based on Fumaric Acid Sludge and Its Application in Oil Well Drilling Fluids.

Fumaric acid sludge (FAS) by-produced from phthalic anhydride production wastewater treatment contains a large amount of refractory organic compounds with a complex composition, which will cause environmental pollution unless it is treated in a deep, harmless manner. FAS included saturated carboxylic acid, more than 60%, and unsaturated carboxylic acid, close to 30%, which accounted for the total mass of dry sludge. A new oil well drilling fluid filtrate loss reducer, poly(AM-AMPS-FAS) (PAAF), was synthesized by copolymerizing FAS with acrylamide (AM) and 2-acrylamide-2-methyl propane sulfonic acid (AMPS). Without a refining requirement for FAS, it can be used as a polymerizable free radical monomer for the synthesis of PAAF after a simple drying process. The copolymer PAAF synthesis process was studied, and the optimal monomer mass ratio was determined to be AM:AMPS:FAS = 1:1:1. The temperature resistance of the synthesized PAAF was significantly improved when 5% sodium silicate was added as a cross-linking agent. The structural characterization and evaluation of temperature and complex saline resistance performance of PAAF were carried out. The FT-IR results show that the structure of PAAF contained amide groups and sulfonic acid groups. The TGA results show that PAAF has good temperature resistance. As an oilfield filtrate loss reducer, the cost-effective copolymer PAAF not only has excellent temperature and complex saline resistance, the API filtration loss (FL) was only 13.2 mL/30 min after 16 h of hot rolling and aging at 150 °C in the complex saline-based mud, which is smaller compared with other filtrate loss reducer copolymers, but it also has little effect on the rheological properties of drilling fluid.