ArticleMaterials (Basel, Switzerland)2022
The Effect of Heat Input, Annealing, and Deformation Treatment on Structure and Mechanical Properties of Electron Beam Additive Manufactured (EBAM) Silicon Bronze.
Article in Materials (Basel, Switzerland), 2022. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 1 paper.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
1 citing paper in PubMed.
- Structure and Mechanical Properties of Cu-Al-Mn Alloys Fabricated by Electron Beam Additive Manufacturing.Materials (Basel, Switzerland) · 2022Article
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
7 authors.
Funding
Abstract
Electron beam additive wire-feed manufacturing of Cu-3wt.%S-0.8wt.%Mn bronze thin wall on a stainless steel substrate has been carried out at heat input levels of 0.19, 0.25, and 0.31 kJ/mm. The microstructures of as-deposited metal ranged from low aspect ratio columnar with equiaxed grain layers to zig-zagged and high aspect ratio columnar, as depended on the heat input. Post-deposition annealing at 900 °C for 6 h resulted in recrystallization of the high aspect ratio columnar grains with further grain growth by boundary migration. Pre-deformation by 10% thickness reduction and then annealing at 900 °C for 6 h also allowed obtaining recrystallized grain structures with less fraction of twin boundaries but higher fraction of high-angle ones, as compared to those of only annealed sample. Pre-deformation and ensuing annealing allowed simultaneous increasing of the ultimate tensile strength and strain-to-fracture.