Effect of Different Hot-Pressing Pressure and Temperature on the Performance of Titanium Mesh-Based MEA for DMFC.
Article in Membranes, 2022. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Not yet cited in PubMed.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
0 citing papers in PubMed.
No citing paper in PubMed yet.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
7 authors.
Funding
Abstract
The hot-pressing process of the membrane electrode assembly (MEA) is one of the research hotspots in the field of the fuel cell. To obtain suitable titanium mesh-based MEA hot pressing process parameters, titanium mesh was used as electrode substrate material. The anode and cathode of MEA were prepared by the drip-coated method, and the titanium mesh-based MEA was prepared under different hot-pressing pressure and temperature, respectively. The performance of titanium mesh-based MEA was studied by morphological observation, elemental analysis, thickness measurement, single cell test and numerical fitting analysis. The results demonstrated that: with increasing hot-pressing pressure from 0 MPa to 10 MPa, the forming thickness of titanium mesh-based MEA is getting thin gradually, and the peak power density of titanium mesh-based MEA first increased and then gradually decreased; with increasing hot-pressing temperature from 115 °C to 155 °C, the peak power density of titanium mesh-based MEA enhanced at the beginning and then also gradually decreased. Under the premise of a hot-pressing time of 180 s and the optimal operating temperature of DMFC of 60 °C, the appropriate hot-pressing process conditions of titanium mesh-based MEA are a hot-pressing pressure of 5 MPa and a hot-pressing temperature of 135 °C. The results can provide a technological reference for the preparation of titanium mesh MEA for DMFC.