Electrical Stability and Piezoresistive Sensing Performance of High Strain-Range Ultra-Stretchable CNT-Embedded Sensors.

Highly flexible and stretchable sensors are becoming increasingly widespread due to their versatile applicability in human/robot monitoring sensors. Conductive polymeric composites have been regarded as potential candidates for such sensors, and carbon nanotubes (CNTs) are widely used to fabricate such composites. In the present study, CNT-embedded high flexible sensors were fabricated using a facile three-roll milling method, which mitigates the drawbacks of the conventional fabrication methods. CNTs content varied between 0.5 and 4.0 wt.%, and the percolation threshold range was obtained via conductivity/resistivity values of the fabricated sensors. Following this, the electrical stability of the sensors was examined against the various DC and AC signals. Furthermore, the fabricated sensors were stretched up to 500% strain, and their sensitivity against varying strain amplitudes was investigated in terms of the change in resistance and gauge factors. Lastly, the fabricated sensors were applied to human fingers for monitoring finger bending and releasing motions to validate their potential applications. The experimental results indicated that these sensors have a percolation threshold of around 2% CNTs content, and the sensors fabricated with 2 to 4% CNTs content showed measurable resistance changes against the applied strain amplitudes of 50-500%. Among these sensors, the sensor with 2% CNTs content showed the highest sensitivity in the studied strain range, exhibiting a resistance change and gauge factor of about 90% and 1.79 against 50% strain amplitude and about 18,500% and 37.07 against 500% strain amplitude, respectively. All these sensors also showed high sensitivity for finger motion detection, showing a resistance change of between 22 and 69%.