Tribological Behaviors of Super-Hard TiAlN Coatings Deposited by Filtered Cathode Vacuum Arc Deposition.
Article in Materials (Basel, Switzerland), 2022. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 2 papers.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
2 citing papers in PubMed.
- Microstructure, Mechanical and Tribological Properties of Arc Ion Plating NbN-Based Nanocomposite Films.Nanomaterials (Basel, Switzerland) · 2022Article
- Improvement of Tribological Performance of TiAlNbN Hard Coatings by Adding AlCrN.Materials (Basel, Switzerland) · 2022Article
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
8 authors.
Funding
Abstract
High hardness improves the material’s load-bearing capacity, resulting in the enhancement of tribological properties. However, the high hardness is difficult to achieve for TiAlN coating due to the transformation of the close-packed structure from cubic to hexagonal and the increase in the grain size when the Al content is high. In the present study, the ultrahard TiAlN coatings (hardness > 40 GPa) are successfully developed by filtered cathodic vacuum arc technology to study the effect of nitrogen flux rate on tribological behaviors. The highest hardness of 46.39 GPa is obtained by tuning the nitrogen flux rate to achieve the regulation of Al content and the formation of nanocrystalline. The stable fcc TiAlN phase is formed via the solid-phase reaction under a high nitrogen concentration, and more aluminum atoms replace the titanium atoms in the (Ti, Al)N solid solution. The high Al content of the Ti0.35Al0.65N coating has a nanocrystalline structure and the average crystalline size is 16.52 nm. The TiAlN coating deposited at a nitrogen flux rate of 60 sccm exhibits the best properties of a combination of microhardness = 2972.91 Hv0.5, H = 46.39 GPa, E = 499.4 Gpa, ratio H/E* = 0.093 and ratio H3/E*2 = 0.403. Meanwhile, the TiAlN coating deposited at 60 sccm shows the lowest average friction coefficient of 0.43 and wear rate of 1.3 × 10−7 mm3 N−1 m−1 due to the best mechanical properties.