Evaluation of Fiber Post Adhesion to Root Dentin Achieved with Different Composite Cements: 1-year In Vitro Results.

purposeTo evaluate push-out bond strength (PBS) and interfacial nanoleakage (NL) of adhesively luted fiber posts using different composite cements and polymerization protocols. MATERIAL AND

methods100 premolars were endodontically treated and assigned to the following groups (n=10): RelyX Universal light-cure (3M Oral Care); RelyX Universal self-cure (3M Oral Care); Maxcem Elite Chroma light-cure (Kerr); Maxcem Elite Chroma self-cure (Kerr); Calibra Universal light-cure (Dentsply Sirona); Calibra Universal self-cure (Dentsply Sirona); Multilink Automix light cure (Ivoclar Vivadent); Multilink Automix self-cure (Ivoclar Vivadent); Luxacore Z Dual light-cure (DMG); Luxacore Z Dual self-cure (DMG). Half of the teeth from each group were subjected to the PBS test after 24 h (T0), while the other half was tested after 12 months (T12) of artificial saliva aging. An additional 4 teeth per group were prepared for NL expression. PBS values were analyzed using multivariate ANOVA and Tukey's post-hoc test. NL scores were analyzed using chi-squared tests (α = 0.05).

resultsStatistical analysis revealed that the variables "cement" and "aging" significantly influenced PBS (p < 0.05), but not "polymerization" and "root region" (p > 0.05). Significantly lower PBS values (p < 0.05) were detected for the Calibra Universal groups compared to other cements, while the RelyX Universal groups performed equally well (p > 0.05) or better than other cements (p < 0.05). At T12, PBS values increased in the majority of groups, irrespective of root region (p < 0.05). Differences in NL expression were present at T0, and in general, the aging process increased marginal infiltration.

conclusionAging and choice of composite cement influenced PBS, while root region and polymerization protocol seemed to have no influence on posts' resistance to dislodgment.