Development and Characterization of Silver-Doped Multi-Walled Carbon Nanotube Membranes for Water Purification Applications.
Article in Membranes, 2022. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 2 papers.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
2 citing papers in PubMed.
- Impact of adding silver-doped carbon nanotube fillers to heat-cured acrylic denture base on flexural strength, contact angle and surface roughness.Scientific reports · 2026Article
- Synthesis and Characterization of Boehmite Particles Obtained from Recycling: Water Disinfection Application.Nanomaterials (Basel, Switzerland) · 2022Article
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
4 authors.
Funding
No grant is acknowledged in the PubMed record.
Abstract
A unique approach was utilized to develop multi-walled carbon nanotube (MWCNT) silver (Ag) membranes. MWCNTs were impregnated with 1 wt% Ag loading, which resulted in a homogeneous dispersion of Ag in MWCNTs. MWCNTs impregnated with Ag were then uniaxially compacted at two different pressures of 80 MPa and 120 MPa to form a compact membrane. Compacted membranes were then sintered at two different temperatures of 800 °C and 900 °C to bind Ag particles with MWCNTs as Ag particles also act as a welding agent for CNTs. The powder mixture was characterized by FESEM, thermogravimetric analysis, and XRD, while the developed samples were characterized by calculating the porosity of membrane samples, contact angle, water flux and a diametral compression test. The developed membranes showed overall large water flux, while maximum porosity was found to decrease as the compaction load and sintering temperature increased. The mechanical strength of the membranes was found to increase as the compaction load increased. The hydrophilicity of the membranes remained unchanged after the addition of Ag particles. The developed membranes would be useful for removing a variety of contaminants from water.