Mechanical and optimization studies of polypropylene hybrid biocomposites.

Towards developing a polymeric matrix characterized by high strength to cost ratio, polypropylene (PP) was hybridized with low-cost particulate snail shell (PSS) and kenaf fiber (KF) via compression moulding at 180 °C and 0.2 MPa. The developed composites were grouped into three and labeled as mix 2, 4, and 10. Each group entailed the blend of 5, 10, 20, and 30 wt% KF with 2, 4, 10 wt% PSS respectively. From the results, it is observed that the hardness value was enhanced by the blend of 5 to 30 wt% KF and 2, 4, and 10 wt% PSS. However, 2 wt% PSS mix with 5 to 30 wt% KF resulted in progressive improvement in impact, compressive, flexural, and tensile strengths values. The 4 wt% PSS yielded consecutive increase in impact, compressive and flexural strength when combined with 5 and 10 wt% KF. However, it was observed that subsequent addition of 20 and 30 wt% KF led to a marginal reduction in the strength values. The tensile strength attained optimum value when 4 wt% PSS was commixed with 30 wt% KF. Conversely, the combinations of 10 wt% PSS with 5, 10, 20, and 30 wt% KF had no significant improvement to the mechanical properties of PSS/KF-bio-PP composite (except for hardness) siring strength decrease. Taguchi optimization revealed that the collage of 4 wt% PSS and 10 wt% KF presented optimum mix for hybrid bio-PP composite.