Effect of Cooling Rate during Glazing on the Mechanical and Optical Properties of Monolithic Zirconia with 3 mol% Yttria Content.

Glazing is the final heat treatment process in the manufacturing of a monolithic zirconia prosthesis. Herein, the effect of cooling rate during zirconia glazing was investigated. A 3 mol% yttria-stabilized tetragonal zirconia polycrystal was glazed at the general cooling rate suggested by the manufacturer, as well as at higher and lower cooling rates, and the differences in flexural strength, hardness, optical properties, and crystal structure were evaluated. A higher cooling rate did not affect the flexural strength, hardness, grain size, optical properties, or crystal structure; however, the Weibull modulus decreased by 1.3. A lower cooling rate did not affect the flexural strength, optical properties, or crystal structure; however, the Weibull characteristic strength increased by 26.7 MPa and the Weibull modulus increased by 0.9. The decrease in hardness and the increase in grain size were statistically significant; however, the numerical differences were negligible. This study revealed that a lower cooling rate provides more reliable flexural strength. Therefore, glazing can proceed at a general cooling rate, which takes 3-4 min; however, glazing at a lower cooling rate will provide a more consistent flexural strength if desired, despite being time-consuming.