Effect of Two Brands of Glaze Material on the Flexural Strength and Probability of Failure of High Translucent Monolithic Zirconia.
Article in Materials (Basel, Switzerland), 2021. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 8 papers.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
8 citing papers in PubMed.
- Effect of Glazing Dwell Time and Cooling Duration on Flexural Strength and Surface Microhardness of 3 mol% Yttria-Stabilized Tetragonal Zirconia: An In Vitro Study.Journal of esthetic and restorative dentistry : official publication of the American Academy of Esthetic Dentistry ... [et al.] · 2026Article
- Load-bearing capacity of knife-edged monolithic zirconia crowns: effect of thickness and fabrication method.Clinical oral investigations · 2026Article
- Effect of different glazing methods on the surface roughness and hardness of zirconia ceramics: an in vitro study.BMC oral health · 2025Article
- Evaluation of the Effect of Chairside Adjustment Extent on the Biaxial Flexural Strength of Aged Monolithic Zirconia.Cureus · 2025Article
- Impact of deglazing on biaxial flexural strength of high translucent zirconia: effect of hydrothermal aging, pH-cycling, and load-cycling.BMC oral health · 2025Article
- Mechanisms of Strength Degradation of Dental Zirconia Due to Glazing: Dependence on Glaze Thickness.Materials (Basel, Switzerland) · 2025Article
- In Vitro Evaluation of Speed Sintering and Glazing Effects on the Flexural Strength and Microstructure of Highly Translucent Multilayered 5 mol% Yttria-Stabilized Zirconia.Materials (Basel, Switzerland) · 2024Article
- Comparative effects of glazing versus polishing on mechanical, optical, and surface properties of zirconia ceramics with different translucencies.Clinical and experimental dental research · 2024Article
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
4 authors.
Funding
No grant is acknowledged in the PubMed record.
Abstract
(1) Background: The effect of glazing on the mechanical properties of monolithic high translucent zirconia is not well reported. Therefore, the purpose of this study was to evaluate the effect of glazing on the flexural strength of high translucent zirconia; (2) Methods: Ninety specimens were prepared from second-generation 3Y-TZP high translucent blocks and divided into three groups. Glaze materials were applied on one surface of the specimen and subjected to a four-point bending test and flexural stress and flexural displacement values were derived. Descriptive fractographic analysis of surfaces was conducted to observe the point of failure and fracture pattern.; (3) Results: Control-nonglazed (647.17, 1σ = 74.71 MPa) presented higher flexural strength values compared to glaze I (541.20, 1σ = 82.91 MPa) and glaze II (581.10, 1σ = 59.41 MPa). Characteristic strength (σ