ArticleACS omega2021
Characteristic and Properties of Ternary Shape-Stabilized Composite Phase Change Materials Based on Expanded Graphite.
Article in ACS omega, 2021. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 2 papers.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
2 citing papers in PubMed.
- Fabrication and thermal performance of ternary fatty acid/expanded graphite form-stable composite phase change materials.iScience · 2026Article
- The Effect of Expanded Graphite Content on the Thermal Properties of Fatty Acid Composite Materials for Thermal Energy Storage.Molecules (Basel, Switzerland) · 2024Article
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
6 authors.
Funding
No grant is acknowledged in the PubMed record.
Abstract
Myristic acid-palmitic acid-tetradecanol/expanded graphite (MA-PA-TD/EG) and myristic acid-stearic acid-lauric acid/ expanded graphite (MA-SA-LA/EG) were obtained. MA-PA-TD/EG and MA-SA-LA/EG for the optimum mass ratio of 8:1 were investigated by DSC, FT-IR, TG, and SEM, and it was shown that MA-PA-TD and MA-SA-LA phase change materials were evenly distributed in expanded graphite through capillary force. Phase transition temperatures of MA-PA-TD/EG and MA-SA-LA/EG before and after cooling and heating cycles were 34.14, 34.39 °C and 30.21, 30.33 °C, respectively, and MA-PA-TD/EG and MA-SA-LA/EG had good stability. On the other hand, MA-PA-TD/EG was 67% faster than that of MA-PA-TD during solid-liquid phase change, and MA-SA-LA/EG was 63% faster than that of MA-SA-LA. Meanwhile, MA-PA-TD/EG and MA-SA-LA/EG had good thermal stability and heat storage according to thermogravimetric experiments. Therefore, MA-PA-TD/EG and MA-SA-LA/EG are suitable for practical application in buildings.
Identifiers