Hybrid Laser Deposition of Composite WC-Ni Layers with Forced Local Cryogenic Cooling.

The purpose of this study was to demonstrate the effect of forced and localized cooling by nitrogen vapours stream under cryogenic conditions during laser deposition of WC-Ni powder on the geometry, microstructure of clad layers and dry sliding wear resistance of the coatings. For this purpose, comparative tests were performed by conventional laser cladding at free cooling conditions in ambient air and by the developed novel process of laser deposition with additional localized cooling of the solidifying deposit by nitrogen vapours stream. Due to presence of gaseous nitrogen in the region of the melt pool and solidifying deposit, the process was considered as combining laser cladding and laser gas nitriding (performed simultaneously), thus the hybrid process. The influence of the heat input and cooling conditions on the geometrical features, dilution rate, share of carbides relative to the matrix, and the fraction share of carbides, as well as hardness profiles on cross sections of single stringer beads was analysed and presented. The XRD, EDS analysis and the sieve test of the experimental powder were used to characterize the composite WC-Ni type powder. The OM, SEM, EDS and XRD test methods were used to study the microstructure, chemical and phase composition of clad layers. Additionally, ball-on-disc tests were performed to determine the wear resistance of representative coatings under dry sliding conditions. The results indicate that the novel demonstrated technique of localized forced cooling of the solidifying deposit has advantageous effect, because it provides approximately 20% lower penetration depth and dilution, decreases tendency for tungsten carbides decomposition, provides more uniform distribution and higher share of massive eutectic W