Investigation on Morphology and Mechanical Properties of Rod Units in Lattice Structures Fabricated by Selective Laser Melting.

Selective laser melting (SLM) fabrication of lattice structures has attracted considerable interest due to its many immanent advantages, such as high specific strength. A wide variety of lattice structures have been designed and fabricated. However, as a vital prerequisite for design optimization, a clear relation between the process constraint of SLM and the apparent properties of the fabricated lattice structure has received much less attention. Therefore, this work systematically investigates the characterization and preformation of rod units, which are the basic components of lattice structures, so as to evaluate the SLM manufacturability of lattice structures. A series of rod units with different inclination angles and diameters were fabricated by SLM. Their morphology and mechanical properties were measured by scanning electron microscope observation and a tensile test, respectively. The inclination angle was found to have significant effects on profile error and little effect on mechanical properties. The higher the inclination angle, the larger the profile error. The characteristic diameter had no significant correlation with profile errors and mechanical properties. Based on systematic studies, a formula is proposed to evaluate the cross-sectional area of the fabricated rod units and further estimate their load capacity. This has important implications for optimizing the design of lattice structures fabricated by SLM.