Variability in stem taper surface topography affects the degree of corrosion and fretting in total hip arthroplasty.
Article in Scientific reports, 2021. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 3 papers.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
3 citing papers in PubMed, 14 citations in OpenAlex.
- Characterization of Micro-Threaded Stem Taper Surfaces of Cementless Hip Endoprostheses.Materials (Basel, Switzerland) · 2024Article
- Surface Analysis of Ti-Alloy Micro-Grooved 12/14 Tapers Assembled to Non-Sleeved and Sleeved Ceramic Heads: A Comparative Study of Retrieved Hip Prostheses.Materials (Basel, Switzerland) · 2023Article
- An Overview of the Stability and Fretting Corrosion of Microgrooved Necks in the Taper Junction of Hip Implants.Materials (Basel, Switzerland) · 2022Review
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
10 authors at 4 institutions in 2 countries.
Funding
No grant is acknowledged in the PubMed record.
Abstract
Degradation at the modular head-neck interface in total hip arthroplasty (THA) is predominately expressed in the form of corrosion and fretting, potentially causing peri-prosthetic failure by adverse reactions to metal debris. This retrieval study aimed to quantify variations in stem taper surface topographies and to assess the influence on the formation of corrosion and/or fretting in titanium alloy stem tapers combined with metal and ceramic heads. Four hip stem designs (Alloclassic, CLS, Bicontact and SL-Plus) were characterized using high-resolution 3D microscopy, and corrosion and fretting were rated using the Goldberg scoring scheme. Quantification of the taper surface topographies revealed a high variability in surface characteristics between threaded stem tapers: Alloclassic and CLS tapers feature deeply threaded trapezoid-shaped profiles with thread heights over 65 µm. The sawtooth-shaped Bicontact and triangular SL-Plus taper are characterized by low thread heights below 14 µm. Significantly lower corrosion and fretting scores were observed in lightly threaded compared to deeply threaded tapers in ceramic head combinations. No significant differences in corrosion or fretting scores with thread height were found in pairings with metal heads. Understanding the relationship between stem taper surface topography and the formation of corrosion and fretting could help to improve the performance of modern THAs and lead to longer-lasting clinical results.