The Quenching and Sonication Effect on the Mechanical Strength of Silver Nanowires Synthesized Using the Polyol Method.

This study aims to determine the effect of fast cooling (quenching) on thermal properties, mechanical strength, morphology and size of the AgNWs. The synthesis of AgNWs was carried out at three different quenching-medium temperatures as follows: at 27 °C (ambient temperature), 0 °C (on ice), and -80 °C (in dry ice) using the polyol method at 130 °C. Furthermore, the AgNWs were sonified for 45 min to determine their mechanical strength. Scanning electron microscopy analysis showed that the quenched AgNWs had decreased significantly; at 27 °C, the AgNWs experienced a change in length from (40 ± 10) to (21 ± 6) µm, at 0 °C from (37 ± 8) to (24 ± 8) µm, and at -80 °C from (34 ± 9) to (29 ± 1) µm. The opposite occurred for their diameter with an increased quenching temperature: at 27 °C from (200 ± 10) to (210 ± 10) nm, at 0 °C from (224 ± 4) to (239 ± 8) nm, and at -80 °C from (253 ± 6) to (270 ± 10) nm. The lower the temperature of the quenching medium, the shorter the length and the higher the mechanical strength of AgNWs. The UV-Vis spectra of the AgNWs showed peak absorbances at 350 and 411 to 425 nm. Thermogravimetric analysis showed that AgNWs quenched at -80 °C have better thermal stability as their mass loss was only 2.88%, while at the quenching temperatures of 27 °C and 0 °C the mass loss was of 8.73% and 4.17%, respectively. The resulting AgNWs will then be applied to manufacture transparent conductive electrodes (TCEs) for optoelectronic applications.